That is something I haven't tried. If I were to do that. I would probably do some test parts, to see just how long the parts could go before the clear was no longer a nice "silver", and then try to optimize the dye conditions.
I do think anodizing at lower current density may be an advantage, it seems to stay a more natural color when thicker coats are done.
|