I watched the powder flow. I use an IR gun but my temps have never exceeded 300F even on warm days. I attributed this to curing with an IR lamp...
Other projects that I have done have been very durable this is my first oops....
It could be that while the powder had enough heat to flow, it didnt have enough cure, since I have no way of increasing temperature (other than fabricating a better encloser) is it possible to cure at lower temp for longer times ? The finish was beautiful, no beading, great gloss...
|