Hi Ken,
Everybody tells me that the copy chrome is identical to triple chrome, including the people at caswell. The shine, durabilty etc . are the same. So if this is the case it seems to me that it would much better suit me to use it.
There are no enviromental issues, you use less amps while plating, the solution is virtually permanant, no fumes.
I think the pros outway the cons, as a matter of fact I don't even see a plus for the triple chrome, but thats just my opinion.
Thanks everybody for your input, I am looking foward to hearing more.
thanks
bob
|