Re: Low temp powders?
I have use some low temp powders
but I don't see any advatages , it's the same as normal powder
drawback I can see are
1 low powder cures at 250 deg , I would be great if it worked for plastics or fiberglass but at 250 it won't ,so that leaves you mostly with metals wich can handle normal cure temps anyway
2 not to many choices of colors
3 more expencive
I belive UV cure powder would be a better choice in some future
|