thick coatings
i was curious as to whether anyone has successfully grown a coating up to 2 to 3 mil thick using the type II LCD method
i have read a few posts by fibergeek saying that he has been able to do it but every time i try i end up having dissolution problems. im wondering whether i am missing somthing
is th 720 rule still used for a coating this thick?
even at 12 ASF, it has reached 1 mil after 60 mins and any time after that i have chalky residue on the piece
i do not need to dye the pieces. the are being used for enginnering machinery.
any suggestions or expierience on the matter would be very helpful as all the anodizing shops here in australia seem to want to keep all the secrets to themselves
|