Re: polished anodize
Without seeing exactly what your trying to achieve, it will be hard to reccommend anything. Experimentation is your friend. Try different ano thicknesses, CD, ano bath temps, polishing methods, sealing methods, etc. There are many variables in anodizing that can be tweaked. Simply polishing the anodize lightly afterward might get what you are looking for.
|