Quote:
|
Originally Posted by mpierich
Holy cr@p, that's the worst case of the pits I've ever seen! You're done polishing, that's for sure.
There may be some kind of hi-temp filler you could use before powdercoating, but if the outgassing continued it prolly wouldn't work.
It's my understanding that these could be filled with a (few?) layers of copper, ground smooth, then plated, if that's the route you wanted to go.
|
Not exactly what I wanted to hear, I guess this is the best they will get. Kind of gives me a bad taste on my first polishing job. They will get Powder Coated. Any powder coating experts out there, that could give me some advice on how this will look.