I have been anodizing for a while now the "old" method. Just wondering about the LCD method. I have a 15-gallon acid bath with a 1-3 acid to water ratio, I keep the temperature around 70 degrees. I run 7 amps per square foot of part area; most runs are about 125 mins per complete paintball gun. From my understanding, the LCD runs at lower amps per square foot. However, I cannot find any info on the method. Most of my results are good, however I get a few parts that look darker "burnt", just wondering if I used a different method, I might get results that are more consistent. Any info would be greatly appreciated.
Thanks,