Have you gotten the faucet replated yet? If not, how bad is the pitting? As the old saying goes, "you can't polish a turd", but if it's not too eaten up, I'd be willing to give it a shot. To get a satin finish, I can glass-bead blast it and then copper plate it, then nickel plate it without a lot of polishing inbetween. That should give it the texture it sounds like you are describing. Let me know here if you are interested. I'm in Columbia, TN (just south of Nashville).
Jay
|