  #1 (permalink)  
Old 11-26-2003, 04:14 PM
Newbie
 
Join Date: Oct 2003
Posts: 35
dsacco1013
Default how much voltage?

When useing the "Hobbist" gun, should you measure the voltage with a voltmeter? And if so should you set it on a AC volt setting or does the box change it to a DC current?


Thanks Dave
Reply With Quote
  #2 (permalink)  
Old 11-26-2003, 04:29 PM
Experienced Metal Finisher
 
Join Date: Sep 2003
Location: CT-NY-NJ area
Posts: 359
non-stick
Default

wow... good question, Dave. I have no clue about the hobbyist gun settings to be totally honest with you. I may be speaking out of line here (somebody correct me if I'm wrong please) but the hobbyist guns are preset at 20KV, aren't they? As for what type of voltage you have.... it's DC current. Basically it's an elaborate system to transform 120 VAC to 20,000 VDC. The industrial guns are no different. Amperage is nil so you don't have to worry about that but, industrial goes up to an adjustable 100KV (one hundred thousand) VDC. I'm betting if your gun is active, the setting is where it should be regardless..... Russ
Reply With Quote
  #3 (permalink)  
Old 11-26-2003, 05:53 PM
Experienced Metal Finisher
 
Join Date: Dec 2002
Location: NJ
Posts: 290
tomg552001
Send a message via AIM to tomg552001
Default

Thats correct, hobby guns are a preset KV :P
Reply With Quote
  #4 (permalink)  
Old 11-26-2003, 06:19 PM
Newbie
 
Join Date: Oct 2003
Posts: 35
dsacco1013
Default

That would explain why I wasnt getting a reading on the AC side of the meter, and I did not try DC. But I wasnt complaining because the powder was "Sticking"....Why ask how kinda thing.

Thanks
Reply With Quote
Reply

Bookmarks


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Trackbacks are Off
Pingbacks are Off
Refbacks are Off

Similar Threads
Thread Thread Starter Forum Replies Last Post
CopyCad & Zinc failure - electrolyte problems? seanc Electroplating Questions 4 11-08-2004 09:16 AM
Voltage movement PeterM Anodizing Questions 2 10-13-2004 04:47 AM
Titanium Anodizing ron423 Anodizing Questions 4 08-23-2004 04:09 PM
Peak voltage question mudwhump Anodizing Questions 6 01-14-2004 10:53 PM


All times are GMT -4. The time now is 03:07 AM.


Powered by vBulletin® Version 3.7.3
Copyright ©2000 - 2008, Jelsoft Enterprises Ltd.
Search Engine Friendly URLs by vBSEO 3.2.0 RC4
Copyright © Caswell Inc.