  • mcaswell
    replied
    Nickel is commonly used for this. Use the Electroless Krome if you want a chrome look, as opposed to a nickel look. Nickel has a slightly yellow hint to it, chrome a slightly blue hint.

    Leave a comment:


  • larry1096
    replied
    Thank you. Would either be more or less appropriate for plating a few firearms?

    Thanks,

    Larry

    Leave a comment:


  • mcaswell
    replied
    About 45, for both, with the Krome being slightly harder.

    Leave a comment:


  • larry1096
    started a topic Hardness Question

    Hardness Question

    I was wondering what your electroless nickel and electroless 'chrome' run as far as hardness. Data referenceing the Rockwell 'C' scale would be much appreciated, as I'm familiar with it.

    Thanks,

    Larry