Re: brass and coldrolled steel
typically speaking no it will not be a problem i am doing a similar job on a 47 springer frontend. there is a lot of factory brazing on this. if you can get it smooth enough then bead blast and powder away. most brazing is done in the 700-1200 degree range so the cure should be no problem. best of luck bro.
Welcome To The Caswell Inc Forums - The Place To Be For Metal Finishing Enthusiasts!
We notice that you are not currently registered on our site, or are not logged in. Registration is FREE and allows you to post questions on our forums, post pictures, access Technical Support, place orders for products and much, much more! Why not take a moment and register? Just click the Register Link above.